Material: High entropy alloy, Superalloy, Copper alloy, Aluminum matrix composite

Standard: ASTM F3049; ISO/ASTM 52907; GB/T 39251-2020

Diameter: 15 μm - 53 μm

Product Detail | Technical Information | Packaging

Product Detail1

Shanghai Metal Corporation is a metal powder for 3D printing manufacturer and supplier.

Metal powders are essential feedstock for additive manufacturing (3D printing) processes like selective laser melting (SLM) and electron beam melting (EBM). They boast precise particle size distributions—typically 15-53 μm for optimal flowability and layer fusion—and high purity (often over 99.9%), ensuring consistent, high-quality printed parts.

Common types include stainless steel powders (ideal for industrial components due to corrosion resistance), titanium alloy powders (widely used in aerospace and medical fields for high strength-to-weight ratio), and nickel-based superalloy powders (suited for high-temperature applications). These powders must meet strict standards: low oxygen content to avoid brittleness, spherical shapes for smooth spreading, and minimal impurities.

With growing demand in aerospace, healthcare, and automotive sectors, metal powders for 3D printing continue to drive innovations in material performance and manufacturing efficiency.

If you want to know more about our metal powder for 3D printing or metal powder for 3D printing’s price, please feel free to contact us, we will reply you within 24 hours.

1.Material: High entropy alloy, Superalloy, Copper alloy, Aluminum matrix composite
2.Standard: ASTM F3049; ISO/ASTM 52907; GB/T 39251-2020;
3.Diameter: 15 μm - 53 μm

High purity and consistency
High material utilization rate
Realize complex structures
Personalized customization

Aerospace
Medical devices
Automobile manufacturing
Energy Heavy Industry

Technical Information of Metal powder for 3D printing:

main products	Aluminum matrix composite
Main grain size range	0-25 μm	15-53 μm	45-105 μm	75-150 μm
mobility	15-53μm	≤80s/50g
Bulk density		≥1.35g/cm3
oxygen content		≤300ppm
nitrogen content		≤200ppm
mechanical property	compressive strength /Mpa 460±20
	yield strength /Mpa 260±20
	Elongation /% 8±2

main products	High entropy alloy
Main grain size range	0-25 μm	15-53 μm	45-105 μm	75-150 μm
mobility	15-53μm	≤30s/50g
Bulk density		≥50% of parent alloy
oxygen content		≤300ppm
nitrogen content		≤300ppm

main products	CuCrZr
Main grain size range	0-25 μm	15-53 μm	45-105 μm	75-150 μm
mobility	15-53μm	≤18s/50g
Bulk density		≥4.3g/cm3
oxygen content		≤200ppm
nitrogen content		≤200ppm

Packing for Metal powder of 3D printing:

Shanghai Metal Corporation Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation. In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.

1)SMC Standard

2)Customization

Case Study

Products & Service

Metal Powder for 3D Printing

Metal